SX780CF钢板规格：厚度：8mm-150mm 宽度：1500mm-2500mm

SX780CF钢板执行标准：WYJ 企标

SX780CF钢板热处理交货状态：淬火+回火（Q+T调制）

淬火：将钢板加热保温后在水油或其他无机盐等介质中进行快速冷却

回火：将钢板在某一适当温度下进行长时间保温在冷却

In March 2015, Wugong steel ranked among eight bidding steel enterprises worldwide in terms of its total score, including product technical quality and price, in the bidding for 780MPa grade hydropower high strength steel of Wudong Hydropower Station.The contract of 11,000 tons of steel for 780MPa grade pressure steel pipe for Wudong Hydropower station is full.Subsequently, the state Grid project in Hebei Fengning, Jilin Donghua two giant hydropower stations 780MPa grade hydropower steel 13,000 tons of orders were also delivered to Wugang production.

SX780CF牌号讲解：高强钢SX780CF牌号表示：”SX“代表三峡的意思。这是舞阳钢铁公司为三峡集团乌东德水电站建设使用780MPa级高强钢SX780CF。这是当前国际上批量应用的水电钢，只有国外少数几家钢企具有批量供货的业绩。

SX780CF钢板可附探伤：也被称为超声波检验，是针对钢板内部质量的一种检验方法手段，同时也可以检验出金属内部的缺陷如隐蔽裂纹、气孔、沙眼和杂质等。

SX780CF化学成分：

化学成分（熔炼分析）%

厚度

C

Si

Mn

P

S

Cr

Ni

Mo

Cu

V

B

小于80mm

0.09

0.5

0.7-1.5

0.015

0.005

0.6

0.5-1.5

0.7

0.5

0.5

0.004

80-120

0.1

120-150

0.11

0.5

0.7-1.5

0.15

0.005

0.7

0.8-1.8

0.7

0.5

0.5

0.004

SX780CF钢板需具备高强韧性、良好冷变形性及焊接性。设备制造要求强度等级高，可焊性能强。由于水电用钢使用环境特殊，对钢板的强度、焊接性能、耐腐蚀性能等要求非常严格。上述钢板力学性能要求在较高的强度下，具备良好的低温冲击韧性、断裂韧性和良好的焊接性能，研发难度极大。

SX780CF力学性能：

厚度

力学性能a横向（机械性能）%

屈服强度

Rp0.2Mpa

抗拉强度

RmMpa

伸长率

bA%

冲击吸收能量

5%应变时效后

冲击吸收能量

试验温度

KV2J

试验温度

KV2J

小于80mm

≥690

770-930

≥15

-40

≥100

-20

≥100

80-120

≧670

750-920

≥15

-40

≥100

-20

≥100